FILARC 118
All-positional, basic AC/DC electrode with 120% recovery for welding steels with min. 680 N/mm2 yield strength;
- g. NAXTRA 70, T1, 80 HLES, HY80 and HY100. Often applied in combination with FILARC 98, where the latter is used for tack welding, root-run welding and for welding standing fillet welds. Use the shortest possible arc. Weave slowly when permitted. A slight weave can be used for standing fillet welds. DC+. Use DC- for root runs.
Classifications: | SFA/AWS A5.5:E11018-M, EN ISO 18275-A:E 69 5 Mn2NiMo B 32 H5 |
Approvals: | CE EN 13479, Seproz UNA 272581, ABS AWS, E11018-M, BV 4Y62 H5, DNV 4Y62 H5, LR 4Y62 H5, MoD (N) Q1N, HY80 |
Approvals are based on factory location. Please contact ESAB for more information.
Welding Current: | AC, DC+- |
Diffusible Hydrogen: | < 5.0 ml/100g |
Alloy Type: | C, Mn, 2%Ni, 0.4%Mo |
Coating Type: | Basic |
Typical Tensile Properties | |||
Condition | Yield Strength | Tensile Strength | Elongation |
ISO | |||
As welded | 740 MPa | 800 MPa | 22 % |
Typical Charpy V-Notch Properties | ||
Condition | Testing Temperature | Impact Value |
ISO | ||
As welded | -50 °C | 80 J |
Typical Weld Metal Analysis % | |||||
C | Mn | Si | Ni | Cr | Mo |
0.06 | 1.65 | 0.32 | 2.27 | 0.06 | 0.44 |
Deposition Data | ||||||
Diameter | Current | Voltage | kg weld metal/ kg electrodes | Number of electrodes/kg weld metal | Fusion time per electrode at 90% I max | Deposition rate 90% I max |
2.5 x 350 mm | 55-105 A | 25.3 V | 0.61 | 83.3 | 46.6 s | 0.93 kg/h |
3.2 x 350 mm | 90-140 A | 22.8 V | 0.56 | 46.2 | 64.3 s | 1.21 kg/h |
4.0 x 450 mm | 110-180 A | 22.8 V | 0.61 | 23.1 | 90.0 s | 1.72 kg/h |
5.0 x 450 mm | 190-280 A | 24.6 V | 0.63 | 13.5 | 90.3 s | 2.75 kg/h |