OK 73.68
OK 73.68 is a 2.5% nickel-alloyed LMA electrode suitable for the welding of low-alloy steels with impact requirements down to
-60°C. The composition of the weld metal is such that good, low-temperature impact properties are obtained, even when welding vertically up. The weld metal of OK 73.68 is also noted for its good corrosion resistance to sea-water and sulphuric acid fumes.
Classifications: | SFA/AWS A5.5:E8018-C1, EN ISO 2560-A:E 46 6 2Ni B 32 H5 |
Approvals: | CE EN 13479, Seproz UNA 272580, NAKS/HAKC 2.5-5.0 mm, ABS 3Y400 H5*, ABS E 8018-C1, BV 5Y40M H5*, DNV 5Y H5*, GL 6Y46 H5*, LR 5Y42m H5*, PRS 5Y 42 H5, RS 5Y46M H5*, VdTÜV 01529 |
* Only up to 4.0 mm. NAKS/HAKC: Valid for lot numbers starting with SB. Approvals are based on factory location. Please contact ESAB for more information.
Welding Current: | AC, DC+ |
Diffusible Hydrogen: | <5.0 ml/100g |
Alloy Type: | 2.5% Ni |
Coating Type: | Lime Basic |
Typical Tensile Properties | |||
Condition | Yield Strength | Tensile Strength | Elongation |
AWS | |||
Stress relieved 1 hr 620 °C | 500 MPa | 600 MPa | 28 % |
ISO | |||
As welded | 540 MPa | 615 MPa | 28 % |
Typical Charpy V-Notch Properties | ||
Condition | Testing Temperature | Impact Value |
AWS | ||
Stress relieved 1 hr 620 °C | -60 °C | 85 J |
ISO | ||
As welded | -60 °C | 105 J |
As welded | -80 °C | 65 J |
Typical Weld Metal Analysis % | |||||
C | Mn | Si | Ni | Cr | Mo |
0.05 | 1 | 0.35 | 2.4 | 0.02 | 0.01 |
Deposition Data | ||||||
Diameter | Current | Voltage | kg weld metal/ kg electrodes | Number of electrodes/kg weld metal | Fusion time per electrode at 90% I max | Deposition rate 90% I max |
2.5 x 350 mm | 70-110 A | 23 V | 0.62 | 70.0 | 55 s | 0.90 kg/h |
3.2 x 450 mm | 105-150 A | 23 V | 0.62 | 32.0 | 81 s | 1.40 kg/h |
4.0 x 450 mm | 140-190 A | 23 V | 0.65 | 21.0 | 88 s | 2.00 kg/h |
5.0 x 450 mm | 190-270 A | 27 V | 0.65 | 13.5 | 104 s | 2.50 kg/h |