Mô tả
OK Autrod 318Si
A continuous, solid, corrosion-resistant, stabilised, chromium-nickel-molybdenum wire for welding Cr-Ni-Mo and Cr-Ni stabailised or non-stabilised steels. OK Autrod 318Si has good general corrosion resistance. The alloy is stabilised with niobium to improve resistance to the intergranular corrosion of the weld metal. The higher silicon content improves the welding properties such as wetting. Due to stabilisation by niobium, this alloy is recommended for service temperatures up to 400ºC.
Classifications Wire Electrode: | EN ISO 14343-A:G 19 12 3 Nb Si, Werkstoffnummer :~1.4576 |
Approvals: | CE EN 13479, NAKS/HAKC 1.2MM, DB 43.039.14, VdTÜV 09735 |
Approvals are based on factory location. Please contact ESAB for more information.
Alloy Type: | Austenitic (with approx. 7 % ferrite) 19% Cr – 12% Ni – 3 % Mo – Nb |
Typical Tensile Properties | |||
Condition | Yield Strength | Tensile Strength | Elongation |
As welded | 460 MPa | 615 MPa | 35 % |
Tested at 400\00B0C. | |||
As welded | 360 MPa | 480 MPa | 35 % |
Typical Charpy V-Notch Properties | ||
Condition | Testing Temperature | Impact Value |
As welded | 20 °C | 100 J |
As welded | -60 °C | 70 J |
Typical Wire Composition % | ||||||||
C | Mn | Si | Ni | Cr | Mo | Cu | Nb | Ferrite FN |
0.05 | 1.7 | 0.8 | 11.9 | 18.8 | 2.60 | 0.10 | 0.50 | 6 |
Deposition Data | ||||
Diameter | Current | Voltage | Wire Feed Speed | Deposition Rate |
0.8 mm | 55-160 A | 15-24 V | 4.0-17.0 m/min | 1.0-4.1 kg/h |
1.0 mm | 80-240 A | 15-28 V | 4.0-16.0 m/min | 1.5-6.0 kg/h |
1.2 mm | 100-300 A | 15-29 V | 3.0-14.0 m/min | 1.6-7.5 kg/h |