OK Autrod 430Ti
A ferritic, stainless, solid wire with a content of 18% Cr and stabilised with 0.5% Ti for welding similar and matching steels. The alloy is also used for cladding on unalloyed and low-alloyed steels. OK Autrod 430Ti is also widely used in the automotive industry for the welding of manifolds, catalytic converters and exhaust pipes.
Classifications Wire Electrode: | EN ISO 14343-A:G Z 17 Ti, Werkstoffnummer :1.4502 |
Approvals: | CE EN 13479 |
Approvals are based on factory location. Please contact ESAB for more information.
Alloy Type: | 18 % Cr – 0.5 % Ti |
Typical Tensile Properties | |||
Condition | Yield Strength | Tensile Strength | Elongation |
Stress relieved 0.5 hr 780 °C | 380 MPa | 580 MPa | 28 % |
Stress relieved 0.5 hr 780 °C | 390 MPa | 600 MPa | 24 % |
Typical Wire Composition % | |||||||
C | Mn | Si | Ni | Cr | Mo | Cu | Ti |
0.07 | 0.5 | 0.9 | 0.3 | 17.6 | 0.05 | 0.10 | 0.400 |
Deposition Data | ||||
Diameter | Current | Voltage | Wire Feed Speed | Deposition Rate |
1.0 mm | 80-190 A | 16-24 V | 2,9-8,4 m/min | 1,1-3,1 kg/h |
1.2 mm | 180-280 A | 20-28 V | 4,9-8,5 m/min | 2,6-4,5 kg/h |
1.6 mm | 230-350 A | 24-28 V | 3,2-5,5 m/min | 3-5,2 kg/h |