OK Flux 10.93
Basic, agglomerated flux for butt welding of stainless steels. A suitable flux for welding of high alloyed CrNi-steels like
- duplex stainless The low Si addition during welding provides good mechanical properties in the weld metal.
Classifications: | EN ISO 14174:S A AF 2 56 54 DC |
Approvals: | CE EN 13479, NAKS/HAKC RD 03-613-03, DB 51.039.10 |
Approvals are based on factory location. Please contact ESAB for more information.
Slag Type: | Fluoride basic CaF2-Al2O3-SiO2 |
Alloy Transfer: | Non alloying |
Density: | nom: 1.0 kg/dm3 |
Basicity Index: | nom: 1.9 |
Flux Consumption | |
Volts | kg Flux / kg Wire DC+ |
26 V | 0.5 kg |
30 V | 0.6 kg |
34 V | 0.8 kg |
38 V | 1.0 kg |
Dimensions | Amps | Travel Speed |
4.0 mm | 580 A | 33 m/h |
Classifications | Wire |
Wire | AWS/EN |
OK Autrod 16.97 | 14343-A:S 18 8 Mn |
OK Autrod 308L | A5.9:ER308L/ 14343-A:S 19 9 L |
OK Autrod 308H | A5.9:ER308H/ 14343-A:S 19 9 H |
OK Autrod 309L | A5.9:ER309L/ 14343-A:S 23 12 L |
OK Autrod 309MoL | A5.9:ER309LMo (mod)/ 14343-A:S 23 12 2 L |
OK Autrod 310MoL | 14343-A:S 25 22 2 N L |
OK Autrod 312 | A5.9:ER312/ 14343-A:S 29 9 |
OK Autrod 316L | A5.9:ER316L/ 14343-A:S 19 12 3 L |
OK Autrod 316H | A5.9:ER316H/ 14343-A:S 19 12 3 H |
OK Autrod 16.38 | 14343-A:S 20 16 3 Mn L |
OK Autrod 317L | A5.9:ER317L/ 14343-A:S 18 15 3 L |
OK Autrod 318 | A5.9:ER318/ 14343-A:S 19 12 3 Nb |
OK Autrod 347 | A5.9:ER347/ 14343-A:S 19 9 Nb |
OK Autrod 385 | A5.9:ER385/ 14343-A:S 20 25 5 Cu L |
OK Autrod 2209 | A5.9:ER2209/ 14343-A:S 22 9 3 N L |
OK Autrod 2307 | 14343-A:S 23 7 N L |
Classifications | Wire |
Wire | AWS/EN |
OK Autrod 2509 | A5.9:ER2594/ 14343-A:S 25 9 4 N L |
OK Autrod 410NiMo | 14343-A:S 13 4 |
Approvals | ||||||||
Wire | ABS | BV | DNV | GL | LR | DB | CE | VdTÜV |
OK Autrod 16.97 | – | – | • | – | – | – | – | – |
OK Autrod 308L | • | • | • | – | – | • | • | • |
OK Autrod 309L | • | – | • | – | • | – | • | • |
OK Autrod 316L | • | – | • | – | – | • | • | • |
OK Autrod 318 | – | – | – | – | – | • | • | • |
OK Autrod 385 | – | – | – | – | – | – | – | • |
OK Autrod 2209 | • | • | • | • | • | – | • | • |
OK Autrod 2509 | – | – | – | – | – | – | • | • |
Typical Mechanical Properties | |||||
Wire | Condition | Yield Strength | Tensile Strength | Elongation | Charpy V-Notch |
OK Autrod 16.97 | As Welded DC+ | 400 MPa | 600 MPa | 45 % | 60 J @ -20°C |
OK Autrod 308L | As Welded DC+ | 400 MPa | 560 MPa | 38 % | 100 J @ 20°C
75 J @ -40°C 65 J @ -60°C 55 J @ -110°C 40 J @ -196°C |
OK Autrod 309L | As Welded DC+ | 430 MPa | 570 MPa | 33 % | 90 J @ 20°C
70 J @ -60°C 60 J @ -110°C 35 J @ -196°C |
OK Autrod 309MoL | As Welded DC+ | 400 MPa | 600 MPa | 38 % | 120 J @ 20°C |
OK Autrod 310MoL | As Welded DC+ | 335 MPa | 575 MPa | 42 % | 120 J @ 20°C |
OK Autrod 316L | As Welded DC+ | 390 MPa | 565 MPa | 42 % | 100 J @ 20°C
95 J @ -40°C 90 J @ -60°C 75 J @ -110°C 40 J @ -196°C |
OK Autrod 16.38 | As Welded DC+ | 410 MPa | 600 MPa | 44 % | 70 J @ -60°C
60 J @ -110°C 40 J @ -196°C |
OK Autrod 317L | As Welded DC+ | 440 MPa | 615 MPa | 28 % | 80 J @ 20°C
50 J @ -60°C |
OK Autrod 318 | As Welded DC+ | 440 MPa | 600 MPa | 42 % | 100 J @ 20°C
90 J @ -60°C 40 J @ -110°C |
Typical Mechanical Properties | |||||
Wire | Condition | Yield Strength | Tensile Strength | Elongation | Charpy V-Notch |
OK Autrod 347 | As Welded DC+ | 455 MPa | 635 MPa | 36 % | 105 J @ 20°C
85 J @ -60°C 60 J @ -110°C 30 J @ -196°C |
OK Autrod 385 | As Welded DC+ | 310 MPa | 530 MPa | 35 % | 80 J @ 20°C |
OK Autrod 2209 | As Welded DC+ | 630 MPa | 780 MPa | 30 % | 140 J @ 20°C
125 J @ -20°C 110 J @ -40°C 80 J @ -60°C |
OK Autrod 2307 | As Welded DC+ | 560 MPa | 730 MPa | 32 % | 140 J @ 20°C
125 J @ -20°C 90 J @ -40°C 60 J @ -60°C |
OK Autrod 2509 | As Welded DC+ | 640 MPa | 840 MPa | 28 % | 85 J @ 20°C
60 J @ -40°C |
OK Autrod 410NiMo | As Welded DC+, 450A, 28V | 900 MPa | 1000 MPa | 15.5 % | 30 J @ 0°C
30 J @ -20°C |
OK Autrod 410NiMo | Stress Relieved DC+, 450A, 28V Stress relieved 600°C, 2h | 770 MPa | 850 MPa | 19 % | 55 J @ 0°C
55 J @ -20°C |
OK Autrod 410NiMo | Stress Relieved DC+, 500A, 30V Stress relieved 580°C, 4h | 785 MPa | 860 MPa | 18 % | 55 J @ 0°C
50 J @ -20°C |
Typical Weld Metal Analysis % | |||||||||
C | Mn | Si | Ni | Cr | Mo | Cu | N | Nb | FN WRC-92 |
OK Autrod 16.97 | |||||||||
0.06 | 6.3 | 1.2 | 8.0 | 18.0 | – | – | – | – | – |
OK Autrod 308L Current: DC+, 420A, 27V | |||||||||
0.02 | 1.4 | 0.6 | 10.0 | 19.5 | – | – | 0.1 | – | 8 |
OK Autrod 308H DC+ | |||||||||
0.05 | 1.5 | 0.6 | 9.9 | 19.9 | – | – | – | – | – |
OK Autrod 309L Current: DC+, 420 A, 27 V | |||||||||
0.02 | 1.3 | 0.5 | 12.5 | 23.0 | – | – | – | – | – |
OK Autrod 309MoL DC+, 420 A, 27 V | |||||||||
0.02 | 1.5 | 0.5 | 14.5 | 20.8 | 2.8 | – | – | – | – |
OK Autrod 310MoL Current: DC+, 420A, 27V | |||||||||
0.02 | 4.0 | 0.1 | 22.0 | 24.5 | 2.1 | – | 0.12 | – | 0 |
OK Autrod 312 Current: DC+, 420A, 27V | |||||||||
0.1 | 1.5 | 0.5 | 9.5 | 29.0 | – | – | – | – | – |
OK Autrod 316L | |||||||||
0.02 | 1.4 | 0.5 | 12.5 | 18.0 | 2.6 | – | – | – | 8 |
Typical Weld Metal Analysis % | |||||||||
C | Mn | Si | Ni | Cr | Mo | Cu | N | Nb | FN WRC-92 |
OK Autrod 316H DC+ | |||||||||
0.05 | 1.5 | 0.6 | 12.5 | 19.0 | 2.2 | – | – | – | – |
OK Autrod 16.38 Current: DC+, 420A, 30V, 30m/h | |||||||||
0.02 | 5.4 | 0.7 | 15.5 | 20.0 | 2.5 | – | 0.13 | – | 0 |
OK Autrod 317L Current: DC+, 420 A, 27 V | |||||||||
0.02 | 1.5 | 0.5 | 13.5 | 18.5 | 3.2 | – | – | – | – |
OK Autrod 318 Current: DC+, 440A, 30V | |||||||||
0.035 | 1.2 | 0.5 | 12.0 | 18.5 | 2.6 | – | – | 0.3 | – |
OK Autrod 347 Current: DC+, 420A, 27V | |||||||||
0.035 | 1.1 | 0.5 | 9.6 | 19.2 | – | – | – | 0.5 | 8 |
OK Autrod 385 Current: DC+, 420A, 27V | |||||||||
0.02 | 1.5 | 0.5 | 25.0 | 19.0 | 4.0 | 1.5 | 0.02 | – | – |
OK Autrod 2209 Current: DC+, 420A, 27V | |||||||||
0.02 | 1.3 | 0.5 | 9.0 | 22.5 | 3.1 | – | 0.17 | – | 45 |
OK Autrod 2307 DC+, 420A, 31V | |||||||||
0.015 | 1.1 | 0.65 | 7.5 | 22.5 | 0.3 | – | 0.12 | – | 40 |
OK Autrod 2509 Current: DC+, 420A, 27V | |||||||||
0.02 | 0.4 | 0.5 | 10.0 | 23.5 | 3.5 | – | 0.19 | – | 40 |
OK Autrod 410NiMo DC+, 450A, 28V | |||||||||
0.02 | 0.4 | 0.5 | 4.1 | 11.7 | 0.51 | – | – | – | – |