OK Flux 10.62
Agglomerated fluoride-basic flux for Submerged Arc Welding. Primarily for multi-run welding. For highest demands on impact properties, low temperature toughness, strength and CTOD-values. Especially suitable for narrow gap welding due to good slag detachability and smooth side-wall blending. For offshore constructions, pressure vessels, power generation, shipbuilding, pipe mills, civil constructions, transport industries, etc. Produces low-oxygen weld metal (approx. 300 ppm) with hydrogen contents maximum 5 ml/100 g, in BlockPac (moisture protection) maximum 4 ml/100g. Operates optimally at the lower end of the voltage range. Designed for single and multi wire procedures, for butt and fillet welds. Works equally well on DC and AC current. Single layer and multi layer welding of unlimited plate thickness.
Classifications: | EN ISO 14174:S A FB 1 55 AC H5,
EN ISO 14174:S A FB 1 55 AC H4 only BlockPac/moisture-protection |
Approvals: | CE EN 13479, NAKS/HAKC RD 03-613-03, DB 51.039.07 |
Approvals are based on factory location. Please contact ESAB for more information.
Diffusible Hydrogen: | max 5 ml H/100g weld metal (Redried flux); max 4 ml H/100g in BlockPac (moisture protection) |
Slag Type: | Fluoride-basic |
Alloy Transfer: | No Silicon or Manganese alloying |
Density: | nom: 1.1 kg/dm3 |
Basicity Index: | nom: 3.2 |
Grain Size (met): | 0.2-1.6 mm (10×65 mesh) |
Flux Consumption | ||
Volts | kg Flux / kg Wire DC+ | kg Flux / kg Wire AC |
26 V | 0.7 kg | 0.6 kg |
30 V | 1.0 kg | 0.9 kg |
34 V | 1.3 kg | 1.2 kg |
38 V | 1.6 kg | 1.4 kg |
Dimensions | Amps | Travel Speed |
Ø 4.0 mm | 580 A | 55 cm/min |
Classifications | Wire | Weld Metal | ||
Wire | AWS/EN | EN – As Welded | AWS – As Welded | AWS – PWHT |
OK Autrod 12.22 | A5.17:EM12K/ 14171-A:S2Si | S 38 5 FB S2Si | A5.17: F7A8-EM12K | A5.17: F6P8-EM12K |
OK Autrod 12.24 | A5.23:EA2/ 14171-A:S2Mo;
24598-A:S S Mo |
S 46 4 FB S2Mo | A5.23: F8A6-EA2-A2 | A5.23: F8P6-EA2-A2 |
OK Autrod 12.32 | A5.17:EH12K/ 14171-A:S3Si | S 46 6 FB S3Si | A5.17: F7A8-EH12K | A5.17: F7P8-EH12K |
OK Autrod 12.34 | A5.23:EA4/ 14171-A:S3Mo;
24598-A:S S MnMo |
S 50 4 FB S3Mo | A5.23: F8A6-EA4-A4 | A5.23: F8P6-EA4-A4 |
OK Autrod 12.40 | A5.17:EH14/ 14171-A:S4 | S 50 4 FB S4 | A5.17: F7A6-EH14 | A5.17: F7P6-EH14 |
Classifications | Wire | Weld Metal | ||
Wire | AWS/EN | EN – As Welded | AWS – As Welded | AWS – PWHT |
OK Autrod 13.10 SC | A5.23:EB2R/
24598-A:S S CrMo1 |
– | – | A5.23: F8P2-EB2R-B2 |
OK Autrod 13.20 SC | A5.23:EB3R/
24598-A:S S CrMo2 |
– | – | A5.23: F8P2-EB3R-B3 |
OK Autrod 13.21 | A5.23:ENi1/ 14171-A:S2Ni1 | S 42 4 FB S2Ni1 | A5.23: F7A6-ENi1-Ni1 | A5.23: F7P8-ENi1-Ni1 |
OK Autrod 13.24 | A5.23:ENi6/
14171-A:S3Ni1Mo0,2 |
S 50 6 FB S3Ni1Mo0.2 | A5.23: F8A10-ENi6-Ni6 | A5.23: F8P8-ENi6-Ni6 |
OK Autrod 13.27 | A5.23:ENi2/ 14171-A:S2Ni2 | S 46 7 FB S2Ni2 | A5.23: F7A10-ENi2-Ni2 | A5.23: F7P10-ENi2-Ni2 |
OK Autrod 13.40 | A5.23:EG/
14171-A:S3Ni1Mo 26304-A:S3Ni1Mo 26304-B:(SUN2M2) |
S 55 6 FB S3Ni1Mo (DC+) | A5.23:F9A8-EG-F3 (DC+) | A5.23: F9P8-EG-F3 |
OK Autrod 13.43 | A5.23:EG/
26304-A:S3Ni2,5CrMo; 26304-B:(SUN4C1M3) |
S 69 6 FB S3Ni2,5CrMo | A5.23: F11A8-EG-G | A5.23: F11P8-EG-G |
OK Autrod 13.49 | A5.23:ENi3/ 14171-A:S2Ni3 | S 46 8 FB S2Ni3 | A5.23: F8A15-ENi3-Ni3 | A5.23: F8P15-ENi3-Ni3 |
Approvals | ||||||||||
Wire | ABS | BV | DNV | GL | LR | DB | CE | RINA | RS | VdTÜV |
OK Autrod 12.22 | • | • | • | • | • | • | • | – | – | • |
OK Autrod 12.24 | – | – | – | – | – | – | • | – | – | • |
OK Autrod 12.32 | • | • | • | • | • | • | • | • | • | • |
OK Autrod 12.34 | • | • | • | • | • | – | – | – | – | – |
OK Autrod 13.10 SC | – | – | – | – | – | • | • | – | – | • |
OK Autrod 13.20 SC | – | – | – | – | – | – | • | – | – | • |
OK Autrod 13.24 | • | • | • | • | • | – | • | – | – | – |
OK Autrod 13.27 | • | • | • | • | • | • | • | • | • | • |
OK Autrod 13.40 | • | • | • | • | • | – | • | – | – | • |
OK Autrod 13.43 | • | • | • | • | • | – | • | – | – | – |
OK Tubrod 15.27S | • | – | • | • | • | – | • | – | – | – |
Typical Mechanical Properties | |||||
Wire | Condition | Yield Strength | Tensile Strength | Elongation | Charpy V-Notch |
OK Autrod 12.22 | As Welded AWS DC+ | 410 MPa | 500 MPa | 33 % | 170 J @ 0°C
160 J @ -20°C 90 J @ -40°C 70 J @ -50°C 35 J @ -62°C |
OK Autrod 12.24 | As Welded AWS DC+ | 500 MPa | 580 MPa | 25 % | 140 J @ 20°C
115 J @ 0°C 80 J @ -20°C 60 J @ -40°C 45 J @ -51°C |
OK Autrod 12.32 | As Welded AWS DC+ | 475 MPa | 560 MPa | 28 % | 175 J @ 20°C
150 J @ 0°C 130 J @ -30°C 110 J @ -40°C 70 J @ -62°C |
OK Autrod 12.34 | As Welded AWS DC+ | 540 MPa | 620 MPa | 24 % | 170 J @ 20°C
160 J @ 0°C 140 J @ -20°C 115 J @ -40°C 45 J @ -51°C |
OK Autrod 12.40 | As Welded AWS DC+ | 530 MPa | 620 MPa | 26 % | 140 J @ 20°C
110 J @ 0°C 80 J @ -20°C 50 J @ -40°C 40 J @ -51°C |
OK Autrod 13.10 SC | Stress relieved 690°C 1.0h AWS DC+ | 500 MPa | 610 MPa | 26 % | 110 J @ -18°C
80 J @ -29°C |
OK Autrod 13.20 SC | Stress relieved 690°C 1.0h AWS DC+ | 525 MPa | 620 MPa | 25 % | 120 J @ -18°C
80 J @ -29°C |
OK Autrod 13.21 | As Welded AWS DC+ | 470 MPa | 560 MPa | 28 % | 195 J @ 20°C
185 J @ 0°C 160 J @ -20°C 70 J @ -40°C 60 J @ -51°C |
OK Autrod 13.24 | As Welded AWS DC+ | 530 MPa | 620 MPa | 25 % | 120 J @ -40°C
110 J @ -50°C 70 J @ -60°C 50 J @ -73°C |
OK Autrod 13.27 | As Welded AWS DC+ | 460 MPa | 570 MPa | 28 % | 140 J @ -20°C
110 J @ -40°C 80 J @ -60°C 50 J @ -73°C |
OK Autrod 13.40 | As Welded AWS DC+ | 610 MPa | 690 MPa | 24 % | 90 J @ -40°C
80 J @ -50°C 50 J @ -62°C |
OK Autrod 13.43 | As Welded AWS DC+ | 700 MPa | 800 MPa | 21 % | 100 J @ -20°C
75 J @ -40°C 65 J @ -50°C 50 J @ -62°C |
OK Autrod 13.49 | As Welded AWS DC+ | 500 MPa | 600 MPa | 27 % | 95 J @ -70°C
40 J @ -101°C |
Typical Weld Metal Analysis % | |||||
C | Mn | Si | Ni | Cr | Mo |
OK Autrod 12.22 DC+, 580A, 29V | |||||
0.07 | 1.0 | 0.30 | – | – | – |
OK Autrod 12.24 DC+, 580A, 29V | |||||
0.07 | 1.0 | 0.22 | – | – | 0.5 |
OK Autrod 12.32 DC+, 580A, 29V | |||||
0.10 | 1.6 | 0.35 | – | – | – |
OK Autrod 12.34 DC+, 580A, 29V | |||||
0.10 | 1.45 | 0.21 | – | – | 0.5 |
OK Autrod 12.40 DC+, 580A, 29V | |||||
0.08 | 1.9 | 0.12 | – | – | – |
OK Autrod 13.10 SC DC+, 580A, 29V | |||||
0.08 | 0.7 | 0.22 | – | 1.1 | 0.5 |
OK Autrod 13.20 SC DC+, 580A, 29V | |||||
0.08 | 0.60 | 0.20 | – | 2.2 | 0.95 |
OK Autrod 13.21 DC+, 580A, 29V | |||||
0.06 | 1.0 | 0.25 | 0.9 | – | – |
OK Autrod 13.24 DC+, 580A, 29V | |||||
0.08 | 1.4 | 0.30 | 0.9 | – | 0.2 |
OK Autrod 13.27 DC+, 580A, 29V | |||||
0.06 | 1.0 | 0.25 | 2.1 | – | – |
OK Autrod 13.40 DC+, 580A, 29V | |||||
0.07 | 1.50 | 0.26 | 0.9 | – | 0.5 |
OK Autrod 13.43 DC+, 580A, 29V | |||||
0.11 | 1.5 | 0.25 | 2.2 | 0.6 | 0.5 |
OK Autrod 13.49 DC+, 580A, 29V | |||||
0.06 | 1.0 | 0.25 | 3.1 | – | – |